Design

These bearings are “built-up” by the welding of relatively large and thick pieces of plates. The design of these bearings must take into account the welding practicality and the access for the welder of all joints that require welding.

Excessive weld sizes or the design of partial and full penetration groove welds when unnecessary should also be avoided. Overdone or unnecessary welding can add extensive costs to these bearings, but add no durability or service life to the bearings.

Since these bearings are very “stiff” and do not have any compressibility under load, thick “shock pads,” such as ½ inch thick preformed-fabric bearing pads, should be placed under these bearings between the concrete bearing seat and the masonry plate.

This is especially recommended on railroad structures where large impact loads are possible.

Both AASHTO and AREMA have requirements for the design of these bearings, which must be considered. As previously stated, many state DOTs and railroad companies have standards for these types of bearings where sizes are varied by the amount of loads expected.

Materials

The plates for these bearings can be ASTM A709 Grades 36, 50, and 50W (AASHTO M270 Grades 36, 50, and 50W).

However, please be aware that for plates over 4 inches in thickness, yield and tensile strengths may be less, or the required steel specification may have to be changed to provide the strength required.

Please contact our engineering staff with any questions on steel over 4 inches thick. Forged or cast steel for the bearings will be considered on demand.

The pins may be simple cold-rolled steel, such as C1018, or can be heat-treated forgings, such as ASTM 688 Classes B through F.

Nuts – recess pin nuts or plain pin nuts – should be of the same material as the steel plates. Cosmec will provide the pins and nuts threaded as required. Various methods, such as the use of cotter pins, can be used to prevent the nuts from loosening with time and rotation.

Grease on the pins and mating parts should be a waterproof medium-consistency grease. Grease fittings for the lubrication of hidden parts can be provided when necessary.

All materials for all US bearings will be certified domestic material, manufactured and fabricated in the USA in accordance with the “Buy American” requirements for all federally funded work.

Coating on the bearings can be the latest high-performance paints, including high-solids zinc primers. The bearing assemblies can also be metallized (zinc or zinc/aluminum thermal spray coatings).

Galvanizing of the carbon steel components can be considered on demand. Coating recommendations can be made to ensure a long-lasting product, no matter the environment.